Effects of thickness reduction in cold rolling process on the formability of sheet metals using ANFIS

Scientific Reports volume 12, Article number: 10434 (2022) Cite this article

1469 Accesses

4 Citations

Metrics details

Cold rolling has detrimental effect on the formability of sheet metals. It is, however, inevitable in producing sheet high quality surfaces. The effects of cold rolling on the forming limits of stretch sheets are not investigated comprehensively in the literature. In this study, a through experimental study is conducted to observe the effect of different cold rolling thickness reduction on the formability of sheet metals. Since the experimental procedure of such tests are costly, an artificial intelligence is also adopted to predict effects of cold thickness reduction on the formability of the sheet metals. In this regard, St14 sheets are examined using tensile, metallography, cold rolling and Nakazima’s hemi-sphere punch experiments. The obtained data are further utilized to train and test an adaptive neural network fuzzy inference system (ANFIS) model. The results indicate that cold rolling reduces the formability of the sheet metals under stretch loading condition. Moreover, the tensile behavior of the sheet alters considerably due to cold thickness reduction of the same sheet metal. The trained ANFIS model also successfully trained and tested in prediction of forming limits diagrams. This model could be used to determine forming limit strains in other thickness reduction conditions. It is discussed that determination of forming limit diagrams is not an intrinsic property of a chemical composition of the sheet metals and many other factors must be taken into account.

Determination of the forming limit of sheet metal is vital in designing final sheet products geometry. It is also one of the main quality control tests in deep drawing and sheet forming factories. In contrast to tensile tests, forming limit determination involves higher numbers of specimen and complicated testing procedure. In attempts to avoid such costly and time consuming tests, there are numerous analytical methods proposed in literature on the calculating FLDs using uniaxial tensile testing curve data1,2,3,4,5. However, uniaxial tensile curves cannot be a reliable source in determination of forming limits6. As Wu et al.7 experimentally showed that sheets with minor differences in uniaxial tensile curves had considerable differences in their FLDs due to the effects of their textures. Therefore, although tensile curves give intuitive sense on forming limits, it is not enough to calculate exact FLDs.

It is currently accepted that the best way to obtain the forming limit curves is experimental tests for every batch of sheet products. The forming limits are dependent on many factors including loading condition, thickness of the sheet as well as microstructural properties of the sheet. There is no model considering all geometrical, loading and microstructural parameters into account. Thus, the models cannot be reliable even they present acceptable results in specific circumstances.

Recently, there has been a rising utilization of artificial intelligence and fuzzy logic in many research fields. The effects of geometrical parameters on the forming limits were examined by Elangovan et al.8 using artificial neural network (ANN). The ANN model was trained using date set obtained from experiments. The trained model was further engaged to predict FLD for a set of new geometrical parameters of the sheet. The behavior of forming limit in different loading and temperature conditions were investigated by Kotkunde et al.9 using ANN. The predicted forming limits using ANN method were in acceptable agreement with experimental outcomes. Extreme thermal and loading rate condition are experimental difficult to apply and examine on the forming limits. In a study by Mohamed et al.10, it is shown that ANN could be employed to predict FLD. Derogar and Djavanroodi11 demonstrated the capability of ANN in sheet metal forming limit predictions.

In another trend in artificial intelligence utilization, Adaptive-Neural-network Fuzzy Inference System (ANFIS) are used to explore the problems involving fuzzy parameters12. This method has been become popular recently in physical modeling. For an account in forming process application, effects of geometrical parameters on the final shape of the part in hole expansion process are studied by Lu et al.13 using ANFIS. The initial dataset for training the ANFIS are gathered using finite element simulations of hole expansion process. The obtained results from trained ANFIS were compared to experimental outcomes. Genetic algorithm and ANFIS models were utilized by Esfahani et al.14 for predicting deformation in laser beam forming. ANFIS manifests remarkable efficiency in achieving accurate results with minor computational costs. There are several instances in literature using ANFIS in evaluations of material characteristics13,15.

Effects of different parameters on the FLD have been investigated in theoretical and experimental studies. However, in most research studies only one or two affecting parameters are considered. Influences of geometries of blank and die16,17,18, strain loading path19, rate of loading20, and lubrication21 were examined as mechanical parameters affecting FLD. On the other hand, second phase particles shape and distribution 22, production history and process23,24, grain size4, material defects25, texture26,27,28 and chemical composition29, are the some metallurgical parameters investigated forming limits determination. In simulations and theoretical modeling, neglecting effect of one parameters might result in considerable error in the FLD calculations.

In recent years, effects of microstructure of sheet material on the forming limit and workability behaviors have been reported. The effect of grain size on the formability of 316L sheets are investigated by Amelirad and Assempour4 using semi-real grain shapes. The simulations was conducted employing crystal plasticity theory30. Xu et al. and directions in single crystal nickel. Int. J. Plast 106, 129–144 (2018)." href="/articles/s41598-022-13694-0#ref-CR31" id="ref-link-section-d223047809e568">31 experimentally examined effect of thickness to grain size ratio on the forming limits and they presented left side of the FLD. It is shown that high values of thickness to grain size ratio had detrimental effect on formability. In another study by Yamaguchi and Mellor, rise in thickness to grain size reduced limit formability of sheets32. Grain refinement in AZ31 is shown to improve ductility. However, formability of AZ31 sheets were independent of grain sizes as demonstrated experimentally by Azghandi et al.33.

Texture effects are extensively examined both experimentally and using crystal plasticity simulations. Wu et al.7 utilized experimental and crystal plasticity approaches to determine forming limit of aluminum sheets. They concluded that even with small difference in tensile behaviors of sheets, difference in textures leads to considerable differences in forming limit curves. Thus, the tensile curve is not a reliable source to predict forming limits without considering other factors such as texture. Barlat28 utilized homogenization methods of polycrystalline aggregate to obtain yield surface of sheet metal. Further, the obtained yield surface was employed to predict forming limits. Barnwal et al.34 demonstrated that forming limits of aluminum sheets were significantly dependent on the texture of the sheets.

To the best of author’s knowledge, influence of cold working on the formability of sheet metals has not been discussed in literature. Therefore, in this study, the application of ANFIS in determining forming limit diagrams using experimental cold rolling data is for St14 steel sheets. Experimental tensile and FLD tests are used to train and test ANFIS models. Afterwards, the trained ANFIS model is employed to predict FLD in other cold rolling conditions. The novelty of this work is to provide a simple neural-fuzzy network which could be used in place of complicated and costly experiments with an acceptable error margin. To the best of author’s knowledge, this is the first time that fuzzy logic is employed to interpret and categorize the input data for prediction of FLD.

St14 low carbon steel sheet are extensively used in forming of automobile bodies due to their high formability. A \(1.5 \pm 0.03{\text{mm}}\) thickness sheet is used in this study to examined formability under different rolling conditions. The chemical composition of the sheet is presented in Table 1. The received sheet were heat treated to alleviate effects of history processes on the sheet. The heat treatment were conducted in 900 °C temperature and sheets were held for 1 h in this temperature. The sheets were cooled to room temperature in furnace. This process results in more homogenous microstructure.

After heat treatment, the sheets were cut into 12 cm width strips and pickled with chloride acid solution to remove oxide scales on the surface. The sheets further cold rolled to 25% and 45% thickness reduction.

Revealing of the microstructure of St14 steel is conducted using metallography procedure. The received specimen, heat treated and rolled ones were cut in rolling direction and sections of the sheets were mounted. Subsequently, the samples were ground using sand paper up to 3000 grit and polished with 1 μm diamond paste. Nital 2% were used to reveal grains in the sample. The results are shown in Fig. 1 for as received samples and in Fig. 2 for treated samples. As observed in Fig. 1, the grain shapes are literally spherical although slight stretch is notice in the overall structure indicating skin pass rolling after spheroidizing process. Thus the microstructure of the as received sheet metal contain spheroidized cementite. Other form of cementite would affect the structure of the sheet metal after heat treatment. After heat treatment the grains grew in size as can be seen in Fig. 2a. The grains have spherical shapes and the trace of spheroidized cementite is not seen after heat treatment indicating extensive decarburization in oxygen atmosphere of the furnace. The cold rolled microstructure is also presented in Fig. 2 for both 25% (Fig. 2b) and 45% (Fig. 2c) thickness reductions. The aim for presenting details of microstructure is its considerable effect on the forming limits such that similar thickness and chemical composition with different grain morphology results in totally different formability. For future comparisons, we believe that it is necessary to report mechanical and metallurgical properties of the sheet and testing condition as far as possible.

Microstructure of St14 sheet in as received condition (100×, Nital 2% for 20 s).

Microstructure of St14 after heat treatment (top), 25% (middle) and 45% (bottom) thickness reduction (100×, Nital 2% for 20 s).

The average grain size in measured to be 1 μm in heat-treated and cold rolled samples.

Tensile testing were conducted according to ASTM E8 standard procedure using sub-size specimens. The engineering stress–strain curves for heat treated samples are shown in Fig. 3. As seen, cold rolling significantly reduces ductility of the sheet and increase yield and ultimate strengths. Due to aging after heat treatment a slight yield point phenomena is seen the sample before rolling. The ductility reduces from 36% strain to 9.5% at rolled samples. Moreover, ultimate strength increases from 256 to 379 MPa and 438 MPa after 25% and 45% thickness reduction in cold rolling, respectively.

St14 uniaxial tensile curves for heat treated samples befor and after cold rolling process.

Nakazima’s hemi-sphere test is utilized to determine forming limit diagrams. The sphere punch was 50 mm in diameter and all the surfaces of the punch and sheet samples were adequately lubricated to minimize friction forces. Samples were cut into bone and rectangular shapes as indicated in Fig. 4. Surface of the samples were grinded to be prepared for etch marking process. Circular and square grid marks were etched on the samples before testing to measure the major and minor principal strains after forming using apparatus shown in Fig. 5. The strains were measured using Myler strip after forming.

Nakazima’s forming limit samples dimensions and cut sheets. The oxide scale on the sheets were due to oxygen containing atomosphere of the furnace which was later grounded before conducting Nakazima tests.

Apparatus to print circular grids on FLD samples.

An example of deformed sample is presented in Fig. 6. At the region around necking and in the necking area the strains of safe and necked point are measured. Subsequently, a forming limit diagram in created using safe points of all deformed samples which represented different loading paths from unidirectional to equal bidirectional stretches. The result of FLD is shown in Fig. 7. Similar to ductility reduction, formability of the sample were significantly decreased in cold rolled sheets, and with increase in thickness reduction the forming limits reaches lower points in the diagram. This in contrast to ductility where increase in thickness reduction have negligible influence on the fracture strain for the experiments conducted in this study.

Forming limit sheet samples after Nakazima’s punch test.

Foming limit curves of St14 steel sheets before and after cold rolling.

Effect of thickness reduction on the St14 sheet metals is modeled using a designed ANFIS network as depicted in Fig. 8. The advantage of using ANFIS is the use of membership functions to categorize input values. For instance, the rolling reduction can be categorized as “extreme” reduction, “moderate” reduction and “skin pass”. On this basis, different responses could be assigned to each category. In ANN, the range of all input values similar to thickness reduction values has to be fitted with the same functions. The input layer consists of three independent parameters of amount of rolling reduction, the value of strain in uniaxial tensile test at necking point and minor strain. Thus, the network has only one output major strain which will be coupled with respective minor strain to indicate a single on the forming limit curve. In the hidden layers, the first layer is called fuzzification layer in which the input values converted to their membership functions values. In total, there is maximum \(3 \times 3 \times 3 = 27\) membership functions:

Schematic of ANFIS layers for three inputs and one outputs.

The input data are assumed to have three categories each.

A schematic view of relationship between rules and membership functions are shown in Fig. 9 for two inputs with 3 membership function categories. For three inputs the graph will be in 3D space. The firing strength of each rule is the combination of the MF values determined by the MF nodes. One instance of the combination is given below:

where RR represents rolling reduction, NS represents necking strain and MS stands for minor strain input values. To have a reasonable effect of each firing strength on the final output the output of each rule nodes are normalized according to the subsequent relation:

for \(j,k = 1{\text{ to }}27\).

Fuzzy subspaces for ANFIS with two-inputs and three MFs.

In the next layer, weighted effects of the real values of the input data is calculated using Takagi and Sugeno’s relation12,35. The effects of the input data is considered to be linear combination of the input values:

Finally, the output is calculated using normalized firing strength and result of the Eq. (4) as given below:

in which \(\mathrm{NR}\) represents number of all rules. This is a straight forward calculation of the input. Similar to the tuning neural networks weights and biases, adjusting membership function constants and Takagi and Sugeno’s relation is adjusted using optimization methods in several epochs. When the error margin satisfied the network is tested using the test split of the data. Caution should be exercised to avoid overfitting the data.

The input data in the ANFIS network described above is the minor strain, strain at necking and thickness reduction of the sheets. The dataset is prepared based on the experimental results of tensile testing and FLD determination. As a rule of thumb for any prediction made by the network there has to be at least 10 times data in the network. In our case, we are aiming to predict one FLD curve which contains at least 5 points (two points on the right side, two points on the left side and one FLD0 point). Therefore, at least 50 sets of data is required to train the ANFIS modelThe input and output data are given in Table 2. Triangle membership functions are considered for fuzzification of the input data:

The parameters \(a\), \(b\) and \(c\) are determined assigned by ANFIS app in Matlab.

In Table 2, 14 set of data are used to train the network and 4 remaining are testing data to ensure about reliability of the network. After iteration, the overall error is 1.9% and the predicted values for bot training and testing data is demonstrated in Fig. 10. As seen, the train network predicts results with high accuracy. The trained network surface for the thickness reduction is shown in.

Comparison of the outputs of ANFIS and experimental values for both training and testing data.

The trained network surface for the thickness reduction is shown in Fig. 11. Using this surface, it is possible to generate new FLD for any thickness reduction other than those given by experiment. Based on the accuracy of trained model, for the case of these material and processing condition, this surface is highly reliable. Similar procedure can be adopted for any other processes in industry. Because the processes in the production line are stable for many circumstances. Another benefit of such networks is simplicity and capability of adjustment using new provided data.

Effects of Thickness reduction in cold rolling process on forming limit curves for St14 sheet steel.

The ANFIS model trained and tests in the previous section is now used to predict FLD under different rolling conditions and the results are compared to the experiments. In Fig. 12, it is shown that forming limit curve generated by ANFIS model is in perfect agreement with the experimental curve. In generating these curves by ANFIS several extra point in minor strain is utilized. This predictions can be generalized to incorporate other parameters in the ANFIS model. In other methods incorporating one more parameters in the calculations results in tremendous time and computational costs while in ANFIS it can be added with minimal effort4,18,24,36,37,38.

Comparison of experimental and simulation forming limits for St14 in different annealing conditions.

In the data selected for the purpose of training and testing ANFIS network, the data of the samples of 35% cold rolled are deliberately dropped. In this section, the trained and tested model is utilized to predict the forming limit curve of the sheet with 35% thickness reduction providing only the values of necking strain and thickness reduction to the network. The output FLD is depicted in Fig. 13 and it is compared with the experimental data and FLD. It is clear that the trained ANFIS model satisfactorily with 6.5% error which is regarded a low error in comparison to other methods of FLD prediction4,26,39.

Effects of Thickness reduction in cold rolling process on forming limit curves for St14 sheet steel.

In this study, the detrimental effect of cold rolling on the formability of sheet metals was examined using experimental tests and neural-fuzzy model. The importance of using ANFIS model, if properly trained, was avoiding time consuming and laborious experimental tasks. To the author’s knowledge, this is the first attempt in engaging ANFIS in prediction of forming limits of sheet metals. The experimental works were conducted using St14 heat treated sheet metals. The sheets were cold rolled to different thickness reduction and tensile, metallography and FLD tests are conducted to determine forming behavior and properties of the sheets. An ANFIS model is also designed to predict effects of cold thickness reduction on the formability of the sheet metals. The obtained data from experiments were utilized to train and test the ANFIS model. The main conclusion of the results are:

Cold rolling of sheets significantly reduces the formability of sheets. Increase in the thickness reduction results in less formability

Experimental methods in determining FLD is costly and proposed models in the literature have not considered all mechanical and microstructural parameters influencing FLD.

Artificial intelligence methods are low cost and light weight method that can incorporate several parameters into consideration.

ANFIS model can include effects of cold rolling in prediction of FLD and the difference between experimental and ANFIS results are negligible.

Assempour, A. et al. A methodology for prediction of forming limit stress diagrams considering the strain path effect. Comput. Mater. Sci. 45(2), 195–204 (2009).

Article CAS Google Scholar

Marciniak, Z. & Kuczyński, K. Limit strains in the processes of stretch-forming sheet metal. Int. J. Mech. Sci. 9(9), 609–620 (1967).

Article Google Scholar

Merklein, M. et al. A new approach to the evaluation of forming limits in sheet metal forming. Key Eng. Mater. https://doi.org/10.4028/www.scientific.net/KEM.639.333 (2015).

Article Google Scholar

Amelirad, O. & Assempour, A. Experimental and crystal plasticity evaluation of grain size effect on formability of austenitic stainless steel sheets. J. Manuf. Process. 47, 310–323 (2019).

Article Google Scholar

Paul, S. K., Manikandan, G. & Verma, R. K. Prediction of entire forming limit diagram from simple tensile material properties. J Strain Anal. Eng. Design 48(6), 386–394 (2013).

Article Google Scholar

Aretz, H. Numerical restrictions of the modified maximum force criterion for prediction of forming limits in sheet metal forming. Modell. Simul. Mater. Sci. Eng. 12(4), 677 (2004).

Article ADS Google Scholar

Wu, P. et al. Crystal plasticity forming limit diagram analysis of rolled aluminum sheets. Metall. Mater. Trans. A. 29(2), 527–535 (1998).

Article Google Scholar

Elangovan, K., Sathiya Narayanan, C. & Narayanasamy, R. Modelling of forming limit diagram of perforated commercial pure aluminium sheets using artificial neural network. Comput. Mater. Sci. 47(4), 1072–1078 (2010).

Article CAS Google Scholar

Kotkunde, N., Deole, A. D. & Gupta, A. K. Prediction of forming limit diagram for Ti-6Al-4V alloy using artificial neural network. Proc. Mater. Sci. 6, 341–346 (2014).

Article CAS Google Scholar

Mohamed, M. et al. Prediction of forming limit diagram for AA5754 using artificial neural network modelling. Key Eng. Mater. 716, 770–778 (2016).

Article Google Scholar

Derogar, A. & Djavanroodi, F. Artificial neural network modeling of forming limit diagram. Mater. Manuf. Processes 26(11), 1415–1422 (2011).

Article CAS Google Scholar

Jang, J. R. ANFIS: Adaptive-network-based fuzzy inference system. IEEE Trans. Syst. Man Cybern. 23(3), 665–685 (1993).

Article Google Scholar

Lu, Y.-H. et al. Study of using ANFIS to the prediction in the bore-expanding process. Int. J. Adv. Manuf. Technol. 26(5–6), 544–551 (2005).

Article Google Scholar

Esfahani, R. T., Golabi, S. & Zojaji, Z. Optimization of finite element model of laser forming in circular path using genetic algorithms and ANFIS. Soft Comput. 20(5), 2031–2045 (2016).

Article Google Scholar

Singh, R., Kainthola, A. & Singh, T. Estimation of elastic constant of rocks using an ANFIS approach. Appl. Soft Comput. 12(1), 40–45 (2012).

Article Google Scholar

Zamanian, H., BOSTAN, S.M., Assempour, A. Initial blank design of deep drawn orthotropic materials using inverse finite element method. (2014).

Feng, F. et al. Effect of die geometry on the formability of 5052 aluminum alloy in electromagnetic impaction deformation. Materials 11(8), 1379 (2018).

Article ADS Google Scholar

Habibi, M. et al. Forming limit diagrams by including the M-K model in finite element simulation considering the effect of bending. Proc. Instit. Mech. Eng. Part L: J Mater. Design Appl. 232(8), 625–636 (2018).

Google Scholar

Wang, H. et al. Experimental and theoretical investigations of the forming limit of 5754O aluminum alloy sheet under different combined loading paths. Int. J. Mech. Sci. 133, 147–166 (2017).

Article Google Scholar

El Fakir, O. et al. Predicting effect of temperature, strain rate and strain path changes on forming limit of lightweight sheet metal alloys. Proc. Eng. 81, 736–741 (2014).

Article CAS Google Scholar

Casari, F. et al. Effect of punch diameter, grid dimension, and lubrication on forming limit diagram. J. Test. Eval. 34(1), 24–30 (2006).

Google Scholar

Ji, Z. et al. Formation process of AZ31B semi-solid microstructures through strain-induced melt activation method. Mater. Charact. 59(7), 905–911 (2008).

Article CAS Google Scholar

Narayanan, S., McDowell, D. L. & Zhu, T. Crystal plasticity model for BCC iron atomistically informed by kinetics of correlated kinkpair nucleation on screw dislocation. J. Mech. Phys. Solids 65, 54–68 (2014).

Article ADS CAS Google Scholar

Habibi, M. et al. Experimental investigation of mechanical properties, formability and forming limit diagrams for tailor-welded blanks produced by friction stir welding. J. Manuf. Process. 31, 310–323 (2018).

Article Google Scholar

Bressan, J. The influence of material defects on the forming ability of sheet metal. J. Mater. Process. Technol. 72(1), 11–14 (1997).

Article Google Scholar

Hajian, M. & Assempour, A. Numerical study on the effects of main BCC rolling texture components on the formability of sheet metals. Int. J. Adv. Manuf. Technol. 80(1–4), 245–253 (2015).

Article Google Scholar

Kuroda, M. Effects of crystallographic texture on plastic flow localization. Key Eng. Mater. https://doi.org/10.4028/www.scientific.net/KEM.340-341.211 (2007).

Article Google Scholar

Barlat, F. Crystallographic texture, anisotropic yield surfaces and forming limits of sheet metals. Mater. Sci. Eng. 91, 55–72 (1987).

Article CAS Google Scholar

Kumar, D. R. Formability analysis of extra-deep drawing steel. J. Mater. Process. Technol. 130, 31–41 (2002).

Article Google Scholar

Amelirad, O. & Assempour, A. Coupled continuum damage mechanics and crystal plasticity model and its application in damage evolution in polycrystalline aggregates. Engineering with Computers. 1–15. https://doi.org/10.1007/s00366-021-01346-2 (2021).

Xu, A. et al. In-situ micro-tensile investigation of strain rate response along< 100> and< 110> directions in single crystal nickel. Int. J. Plast 106, 129–144 (2018).

Article CAS Google Scholar

Yamaguchi, K. & Mellor, P. Thickness and grain size dependence of limit strains in sheet metal stretching. Int. J. Mech. Sci. 18(2), 85–90 (1976).

Article Google Scholar

Azghandi, S. H. M., Weiss, M. & Barnett, M. R. The effect of grain size on the bend forming limits in AZ31 Mg alloy. JOM 72(7), 2586–2596 (2020).

Article ADS CAS Google Scholar

Barnwal, V. K. et al. Effect of microstructure and texture on forming behaviour of AA-6061 aluminium alloy sheet. Mater. Sci. Eng., A 679, 56–65 (2017).

Article CAS Google Scholar

Takagi, T. & Sugeno, M. Fuzzy identification of systems and its applications to modeling and control. IEEE Trans. Syst. Man Cybern. 1, 116–132 (1985).

Article Google Scholar

Ghazanfari, A. et al. Prediction of FLD for sheet metal by considering through-thickness shear stresses. Mech. Based Des. Struct. Mach. 48(6), 755–772 (2020).

Article Google Scholar

Habibi, M., Ghazanfari, A., Asempour, A. et al. Determination of forming limit diagram using two modified finit element models. AmirKabir J. Mech. Eng. 48(4), 141–144 (2017).

Google Scholar

Ghazanfari, A. et al. Investigation on the effective range of the through thickness shear stress on forming limit diagram using a modified Marciniak-Kuczynski model. Modares Mech. Eng. 16(1), 137–143 (2016).

Google Scholar

Hajian, M. & Assempour, A. Experimental and numerical determination of forming limit diagram for 1010 steel sheet: A crystal plasticity approach. Int. J. Adv. Manuf. Technol. 76(9–12), 1757–1767 (2015).

Article Google Scholar

Download references

College of Humanities and Education, Xijing University, Xi’an, 710123, Shaanxi, People’s Republic of China

Yichen Xie

Shanghai Jianqiao University, Shanghai, 201306, People’s Republic of China

Yuping Wu

Faculty of Agriculture, Biosystems Engineering Department, University of Tabriz, Tabriz, Iran

Arman Jalali

School of Engineering, University of Science and Technology Beijing, Beijing, 100083, People’s Republic of China

Huajie Zhou

College of Engineering, Civil Engineering Department, Prince Sattam Bin Abdulaziz University, Al-Kharj, 16273, Saudi Arabia

Mohamed Amine Khadimallah

Laboratory of Systems and Applied Mechanics, Polytechnic School of Tunisia, University of Carthage, Tunis, Tunisia

Mohamed Amine Khadimallah

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

Yichen Xie conducted additional FLD tests and reported the results.Youping Wu elaborated the ANFIS method application and wrote the manuscript.Arman Jalali contributed in the neural network design and modificationHuajie Zhou wrote the main manuscript, prepared tables and figures and performed analyses.Mohamed Amine Khadimallah contributed in the theoretical background of formability of sheet metals and design of experimentsAll authors reviewed the manuscript.

Correspondence to Yuping Wu or Arman Jalali.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Xie, Y., Wu, Y., Jalali, A. et al. Effects of thickness reduction in cold rolling process on the formability of sheet metals using ANFIS. Sci Rep 12, 10434 (2022). https://doi.org/10.1038/s41598-022-13694-0

Download citation

Received: 27 December 2021

Accepted: 26 May 2022

Published: 21 June 2022

DOI: https://doi.org/10.1038/s41598-022-13694-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Scientific Reports (2023)

Journal of Materials Science (2023)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.